Unit
|
Property
|
Test Condition
|
|
g/10min
|
Melt Flow Index
|
ASTM D1238
200℃, 5kg load
|
6.0
|
g/10min
|
Melt Flow Index
|
ASTM D1238
200℃, 10kg load
|
45
|
kg-cm/cm
|
1/2 ⁿ Izod Impact Strength
|
ASTM D256
A method, notched
1/2 ⁿ×1/2 ⁿ×5/2ⁿ
|
14
|
kg-cm/cm
|
1/8ⁿ Izod Impact Strength
|
ASTM D256
A method, notched
1/8 ⁿ×1/2 ⁿ×5/2ⁿ
|
18
|
kg/cm2
|
Tensile Strength At Yield
|
ASTM D638
23℃, 1/8 ⁿ sample
|
400
|
kg/cm2
|
Tensile Strength At
Break
|
ASTM D638
23℃, 1/8 ⁿ sample
|
350
|
%
|
Elongation At Break
|
ASTM D638
23℃
|
30
|
kg/cm2
|
Flexural Yield
|
ASTM D790
23℃, 2.8mm/min
|
750
|
kg/cm2
|
Flexural Modulus
|
ASTM D790
23℃, 2.8mm/min
|
27000
|
℃
|
Heat Distortion Temperature
|
ASTM D648
Unannealed
1/2 in, 18.56 kg/cm2 load pressure
|
84
|
℃
|
Vicat Softening Temperature
|
ASTM D1525
1/8 in, 1 kg load
|
98
|
|
Specific Gravity
|
ASTM D792
|
1.03
|
R-scale
|
Rockwell Hardness
|
ASTM D785
|
107
|