單位
|
性質
|
試驗條件
|
|
g/10min
|
流動指數
|
ASTM D1238
200℃, 5kg load
|
5.0
|
g/10min
|
流動指數
|
ASTM D1238
200℃, 10kg load
|
45
|
kg-cm/cm
|
1/2 ⁿ Izod耐衝擊指數
|
ASTM D256
A method, notched
1/2 ⁿ×1/2 ⁿ×5/2ⁿ
|
17
|
kg-cm/cm
|
1/8ⁿ Izod耐衝擊指數
|
ASTM D256
A method, notched
1/8 ⁿ×1/2 ⁿ×5/2ⁿ
|
20
|
kg/cm2
|
抗張強度-降伏點
|
ASTM D638
23℃, 1/8 ⁿ sample
|
380
|
kg/cm2
|
抗張強度-斷裂點
|
ASTM D638
23℃, 1/8 ⁿ sample
|
300
|
%
|
伸張率-斷裂點
|
ASTM D638
23℃
|
20
|
kg/cm2
|
抗折強度
|
ASTM D790
23℃, 2.8mm/min
|
600
|
kg/cm2
|
抗折係數
|
ASTM D790
23℃, 2.8mm/min
|
22000
|
℃
|
熱變形溫度
|
ASTM D648
(未退火)
1/2 in, 18.56 kg/cm2 load pressure
|
77
|
℃
|
Vicat 軟化溫度
|
ASTM D1525
1/8 in, 1 kg load
|
94
|
|
比重
|
ASTM D792
|
1.17
|
R-scale
|
洛氏硬度
|
ASTM D785
|
102
|